Bone regeneration is a complex, well-orchestrated physiological process of bone formation, which can be seen during normal fracture healing, and is involved in continuous remodelling throughout adult life. However, there are complex clinical conditions in which bone regeneration is required in large quantity, such as for skeletal reconstruction of large bone defects created by trauma, infection, tumour resection and skeletal abnormalities, or cases in which the regenerative process is compromised, including avascular necrosis, atrophic non-unions and osteoporosis. Currently, there is a plethora of different strategies to augment the impaired or ‘insufficient’ bone-regeneration process, including the ‘gold standard’ autologous bone graft, free fibula vascularised graft, allograft implantation, and use of growth factors, osteoconductive scaffolds, osteoprogenitor cells and distraction osteogenesis. Improved ‘local’ strategies in terms of tissue engineering and gene therapy, or even ‘systemic’ enhancement of bone repair, are under intense investigation, in an effort to overcome the limitations of the current methods, to produce bone-graft substitutes with biomechanical properties that are as identical to normal bone as possible, to accelerate the overall regeneration process, or even to address systemic conditions, such as skeletal disorders and osteoporosis.
Bone possesses the intrinsic capacity for regeneration as part of the repair process in response to injury, as well as during skeletal development or continuous remodelling throughout adult life [1,2]. Bone regeneration is comprised of a well-orchestrated series of biological events of bone induction and conduction, involving a number of cell types and intracellular and extracellular molecular-signalling pathways, with a definable temporal and spatial sequence, in an effort to optimise skeletal repair and restore skeletal function [2,3]. In the clinical setting, the most common form of bone regeneration is fracture healing, during which the pathway of normal fetal skeletogenesis, including intramembranous and endochondral ossification, is recapitulated . Unlike in other tissues, the majority of bony injuries (fractures) heal without the formation of scar tissue, and bone is regenerated with its pre-existing properties largely restored, and with the newly formed bone being eventually indistinguishable from the adjacent uninjured bone . However, there are cases of fracture healing in which bone regeneration is impaired, with, for example, up to 13% of fractures occurring in the tibia being associated with delayed union or fracture non-union . In addition, there are other conditions in orthopaedic surgery and in oral and maxillofacial surgery in which bone regeneration is required in large quantity (beyond the normal potential for self-healing), such as for skeletal reconstruction of large bone defects created by trauma, infection, tumour resection and skeletal abnormalities, or cases in which the regenerative process is compromised, including avascular necrosis and osteoporosis.
For all the aforementioned cases in which the normal process of bone regeneration is either impaired or simply insufficient, there are currently a number of treatment methods available in the surgeon’s armamentarium, which can be used either alone or in combination for the enhancement or management of these complex clinical situations, which can often be recalcitrant to treatment, representing a medical and socioeconomic challenge. Standard approaches widely used in clinical practice to stimulate or augment bone regeneration include distraction osteogenesis and bone transport [6,7], and the use of a number of different bone-grafting methods, such as autologous bone grafts, allografts, and bone-graft substitutes or growth factors [8,9]. An alternative method for bone regeneration and reconstruction of long-bone defects is a two-stage procedure, known as the Masquelet technique. It is based on the concept of a “biological” membrane, which is induced after application of a cement spacer at the first stage and acts as a ‘chamber’ for the insertion of non-vascularised autograft at the second stage . There are even non-invasive methods of biophysical stimulation, such as low-intensity pulsed ultrasound (LIPUS) and pulsed electromagnetic fields (PEMF) [11–13], which are used as adjuncts to enhance bone regeneration.
During distraction osteogenesis and bone transport, bone regeneration is induced between the gradually distracted osseous surfaces. A variety of methods are currently used to treat bone loss or limb-length discrepancies and deformities, including external fixators and the Ilizarov technique [6,7], combined unreamed intramedullary nails with external monorail distraction devices , or intramedullary lengthening devices . However, these methods are technically demanding and have several disadvantages, including associated complications, requirement for lengthy treatment for both the distraction (1 mm per day) and the consolidation period (usually twice the distraction phase), and effects on the patient’s psychology and well-being [6,7].
Bone grafting is a commonly performed surgical procedure to augment bone regeneration in a variety of orthopaedic and maxillofacial procedures, with autologous bone being considered as the ‘gold standard’ bone-grafting material, as it combines all properties required in a bone-graft material: osteoinduction (bone morphogenetic proteins (BMPs) and other growth factors), osteogenesis (osteoprogenitor cells) and osteoconduction (scaffold) . It can also be harvested as a tricortical graft for structural support , or as a vascularised bone graft for restoration of large bone defects  or avascular necrosis . A variety of sites can be used for bone-graft harvesting, with the anterior and posterior iliac crests of the pelvis being the commonly used donor sites. Recently, with the development of a new reaming system, the reamer-irrigator-aspirator (RIA), initially developed to minimise the adverse effects of reaming during nailing of long-bone fractures, the intramedullary canal of long bones has been used as an alternative harvesting site, providing a large volume of autologous bone graft . Furthermore, because it is the patient’s own tissue, autologous bone is histocompatible and non-immunogenic, reducing to a minimum the likelihood of immunoreactions and transmission of infections. Nevertheless, harvesting requires an additional surgical procedure, with well-documented complications and discomfort for the patient, and has the additional disadvantages of quantity restrictions and substantial costs [20–22].
An alternative is allogeneic bone grafting, obtained from human cadavers or living donors, which bypasses the problems associated with harvesting and quantity of graft material. Allogeneic bone is available in many preparations, including demineralised bone matrix (DBM), morselized and cancellous chips, corticocancellous and cortical grafts, and osteochondral and whole-bone segments, depending on the recipient site requirements. Their biological properties vary, but overall, they possess reduced osteoinductive properties and no cellular component, because donor grafts are devitalised via irradiation or freeze-drying processing . There are issues of immunogenicity and rejection reactions, possibility of infection transmission, and cost [8,23].
Bone-graft substitutes have also been developed as alternatives to autologous or allogeneic bone grafts. They consist of scaffolds made of synthetic or natural biomaterials that promote the migration, proliferation and differentiation of bone cells for bone regeneration. A wide range of biomaterials and synthetic bone substitutes are currently used as scaffolds, including collagen, hydroxyapatite (HA), β-tricalcium phosphate (β-TCP) and calcium-phosphate cements, and glass ceramics [8,23], and the research into this field is ongoing. Especially for reconstruction of large bone defects, for which there is a need for a substantial structural scaffold, an alternative to massive cortical auto- or allografts is the use of cylindrical metallic or titanium mesh cages as a scaffold combined with cancellous bone allograft, DBM or autologous bone [24,25].
Most of the current strategies for bone regeneration exhibit relatively satisfactory results. However, there are associated drawbacks and limitations to their use and availability, and even controversial reports about their efficacy and cost-effectiveness. Furthermore, at present there are no heterologous or synthetic bone substitutes available that have superior or even the same biological or mechanical properties compared with bone. Therefore, there is a necessity to develop novel treatments as alternatives or adjuncts to the standard methods used for bone regeneration, in an effort to overcome these limitations, which has been a goal for many decades. Even back in the 1950s, Professor Sir Charnley, a pioneer British orthopaedic surgeon, stated that ‘practically all classical operations of surgery have now been explored, and unless some revolutionary discovery is made which will put the control of osteogenesis in the surgeon’s power, no great advance is likely to come from modification of their detail’ .
Since then, our understanding of bone regeneration at the cellular and molecular level has advanced enormously, and is still ongoing. New methods for studying this process, such as quantitative three-dimensional microcomputed tomography analyses, finite element modelling, and nanotechnology have been developed to further evaluate the mechanical properties of bone regenerate at the microscopic level. In addition, advances made in cellular and molecular biology have allowed detailed histological analyses, in vitro and in vivo characterisation of bone-forming cells, identification of transcriptional and translational profiles of the genes and proteins involved in the process of bone regeneration and fracture repair, and development of transgenic animals to explore the role of a number of genes expressed during bone repair, and their temporal and tissue-specific expression patterns . With the ongoing research in all related fields, novel therapies have been used as adjuncts or alternatives to traditional bone-regeneration methods. Nevertheless, the basic concept for managing all clinical situations requiring bone regeneration, particularly the complex and recalcitrant cases, remains the same, and must be applied. Treatment strategies should aim to address all (or those that require enhancement) prerequisites for optimal bone healing, including osteoconductive matrices, osteoinductive factors, osteogenic cells and mechanical stability, following the ‘diamond concept’ suggested for fracture healing (Figure (Figure1)1) .
With improved understanding of fracture healing and bone regeneration at the molecular level , a number of key molecules that regulate this complex physiological process have been identified, and are already in clinical use or under investigation to enhance bone repair.
Of these molecules, BMPs have been the most extensively studied, as they are potent osteoinductive factors. They induce the mitogenesis of mesenchymal stem cells (MSCs) and other osteoprogenitors, and their differentiation towards osteoblasts. Since the discovery of BMPs, a number of experimental and clinical trials have supported the safety and efficacy of their use as osteoinductive bone-graft substitutes for bone regeneration. With the use of recombinant DNA technology, BMP-2 and BMP-7 have been licensed for clinical use since 2002 and 2001 respectively . These two molecules have been used in a variety of clinical conditions including non-union, open fractures, joint fusions, aseptic bone necrosis and critical bone defects . Extensive research is ongoing to develop injectable formulations for minimally invasive application, and/or novel carriers for prolonged and targeted local delivery .
Other growth factors besides BMPs that have been implicated during bone regeneration, with different functions in terms of cell proliferation, chemotaxis and angiogenesis, are also being investigated or are currently being used to augment bone repair [32,33], including platelet-derived growth factor, transforming growth factor-β, insulin-like growth factor-1, vascular endothelial growth factor and fibroblast growth factor, among others . These have been used either alone or in combinations in a number of in vitro and in vivostudies, with controversial results [32,33]. One current approach to enhance bone regeneration and soft-tissue healing by local application of growth factors is the use of platelet-rich plasma, a volume of the plasma fraction of autologous blood with platelet concentrations above baseline, which is rich in many of the aforementioned molecules .
‘Orthobiologics’ and the overall concept to stimulate the local ‘biology’ by applying growth factors (especially BMPs, because these are the most potent osteoinductive molecules) could be advantageous for bone regeneration or even for acceleration of normal bone healing to reduce the length of fracture treatment. Their clinical use, either alone or combined with bone grafts, is constantly increasing. However, there are several issues about their use, including safety (because of the supraphysiological concentrations of growth factors needed to obtain the desired osteoinductive effects), the high cost of treatment, and more importantly, the potential for ectopic bone formation .
Currently BMPs are also being used in bone-tissue engineering, but several issues need to be further examined, such as optimum dosage and provision of a sustained, biologically appropriate concentration at the site of bone regeneration, and the use of a ‘cocktail’ of other growth factors that have shown significant promising results in preclinical and early clinical investigation  or even the use of inhibitory molecules in an effort to mimic the endogenous ‘normal’ growth-factor production. Nanoparticle technology seems to be a promising approach for optimum growth-factor delivery in the future of bone-tissue engineering . Nevertheless, owing to gaps in the current understanding of these factors, it has not been possible to reproduce in vivo bone regeneration in the laboratory.
An adequate supply of cells (MSCs and osteoprogenitors) is important for efficient bone regeneration. The current approach of delivering osteogenic cells directly to the regeneration site includes use of bone-marrow aspirate from the iliac crest, which also contains growth factors. It is a minimally invasive procedure to enhance bone repair, and produces satisfactory results . However, the concentration and quality of MSCs may vary significantly, depending on the individual (especially in older people) [38,39], the aspiration sites and techniques used , and whether further concentration of the bone marrow has been performed , as bone-marrow aspiration concentrate (BMAC) is considered to be an effective product to augment bone grafting and support bone regeneration [40,41]. Overall, however, there are significant ongoing issues with quality control with respect to delivering the requisite number of MSCs/osteoprogenitors to effect adequate repair responses .
Issues of quantity and alternative sources of MSCs are being extensively investigated. Novel approaches in terms of cell harvesting, in vitro expansion and subsequent implantation are promising [42–44], because in vitro expansion can generate a large number of progenitor cells. However, such techniques add substantial cost and risks (such as contamination with bacteria or viruses), may reduce the proliferative capacity of the cells and are time-consuming requiring two-stage surgery . This strategy is already applied for cartilage regeneration . Alternative sources of cells, which are less invasive, such as peripheral blood  and mesenchymal progenitor cells from fat , muscle, or even traumatised muscle tissue after debridement , are also under extensive research. However, the utility of fat-derived MSCs for bone-regeneration applications is debatable, with some studies showing them to be inferior to bone-marrow-derived MSCs in animal models [50,51], and the evidence for a clinically relevant or meaningful population of circulating MSCs also remains very contentious .
It is fair to say that the role of MSCs in fracture repair is still in its infancy, largely due to a lack of studies into the biology of MSCs in vivo in the fracture environment. This to a large extent relates to the historical perceived rarity of ‘in vivo MSCs’ and also to a lack of knowledge about in vivo phenotypes. The in vivophenotype of bone-marrow MSCs has been recently reported  and, even more recently, it has been shown that this population was actually fairly abundant in vivo in normal and pathological bone . This knowledge opens up novel approaches for the characterisation and molecular profiling of MSCs in vivo in the fracture environment. This could be used to ultimately improve outcomes of fracture non-union based on the biology of these key MSC reparative cells.
Although they lack osteoinductive or osteogenic properties, synthetic bone substitutes and biomaterials are already widely used in clinical practice for osteoconduction. DBM and collagen are biomaterials, used mainly as bone-graft extenders, as they provide minimal structural support . A large number of synthetic bone substitutes are currently available, such as HA, β-TCP and calcium-phosphate cements, and glass ceramics [8,23]. These are being used as adjuncts or alternatives to autologous bone grafts, as they promote the migration, proliferation and differentiation of bone cells for bone regeneration. Especially for regeneration of large bone defects, where the requirements for grafting material are substantial, these synthetics can be used in combination with autologous bone graft, growth factors or cells . Furthermore, there are also non-biological osteoconductive substrates, such as fabricated biocompatible metals (for example, porous tantalum) that offer the potential for absolute control of the final structure without any immunogenicity .
Research is ongoing to improve the mechanical properties and biocompatibility of scaffolds, to promote osteoblast adhesion, growth and differentiation, and t0 allow vascular ingrowth and bone-tissue formation. Improved biodegradable and bioactive three-dimensional porous scaffolds  are being investigated, as well as novel approaches using nanotechnology, such as magnetic biohybrid porous scaffolds acting as a crosslinking agent for collagen for bone regeneration guided by an external magnetic field , or injectable scaffolds for easier application .
The tissue-engineering approach is a promising strategy added in the field of bone regenerative medicine, which aims to generate new, cell-driven, functional tissues, rather than just to implant non-living scaffolds . This alternative treatment of conditions requiring bone regeneration could overcome the limitations of current therapies, by combining the principles of orthopaedic surgery with knowledge from biology, physics, materials science and engineering, and its clinical application offers great potential [58,59]. In essence, bone-tissue engineering combines progenitor cells, such as MSCs (native or expanded) or mature cells (for osteogenesis) seeded in biocompatible scaffolds and ideally in three-dimensional tissue-like structures (for osteoconduction and vascular ingrowth), with appropriate growth factors (for osteoinduction), in order to generate and maintain bone . The need for such improved composite grafts is obvious, especially for the management of large bone defects, for which the requirements for grafting material are substantial . At present, composite grafts that are available include bone synthetic or bioabsorbable scaffolds seeded with bone-marrow aspirate or growth factors (BMPs), providing a competitive alternative to autologous bone graft .
Several major technical advances have been achieved in the field of bone-tissue engineering during the past decade, especially with the increased understanding of bone healing at the molecular and cellular level, allowing the conduction of numerous animal studies and of the first pilot clinical studies using tissue-engineered constructs for local bone regeneration. To date, seven human studies have been conducted using culture-expanded, non-genetically modified MSCs for regeneration of bone defects: two studies reporting on long bones and five on maxillofacial conditions . Even though they are rather heterogeneous studies and it is difficult to draw conclusive evidence from them, bone apposition by the grafted MSCs was seen, but it was not sufficient to bridge large bone defects. Furthermore, the tissue-engineering approach has been used to accelerate the fracture-healing process or to augment the bone-prosthesis interface and prevent aseptic loosening in total joint arthroplasty, with promising results regarding its efficacy and safety [62,63].
Recently, an animal study has shown the potential for prefabrication of vascularised bioartificial bone graftsin vivo using β-TCP scaffolds intraoperatively filled with autogenous bone marrow for cell loading, and implanted into the latissimus dorsi muscle for potential application at a later stage for segmental bone reconstruction, introducing the principles of bone transplantation with minimal donor-site morbidity and no quantity restrictions .
Overall, bone-tissue engineering is in its infancy, and there are many issues of efficacy, safety and cost to be addressed before general clinical application can be achieved. Cultured-expanded cells may have mutations or epigenetic changes that could confer a tumour-forming potential . However, in vitro and in vivoevidence suggests that the risk of tumour formation is minimal . No cases of tumour transformation were reported in 41 patients (45 joints) after autologous bone-marrow-derived MSC transplantation for cartilage repair, who were followed for up to 11 years and 5 months . Another important issue is the difficulty of achieving an effective and high-density cell population within three-dimensional biodegradable scaffolds . Consequently, numerous bioreactor technologies have been investigated, and many others should be developed . Their degradation properties should also preserve the health of local tissues and the continuous remodelling of bone . Three-dimensional porous scaffolds with specific architectures at the nano, micro and macro scale for optimum surface porosity and chemistry, which enhance cellular attachment, migration, proliferation and differentiation, are undergoing a continuous evaluation process.
Another promising method of growth-factor delivery in the field of bone-tissue engineering is the application of gene therapy [68,69]. This involves the transfer of genetic material into the genome of the target cell, allowing expression of bioactive factors from the cells themselves for a prolonged time. Gene transfer can be performed using a viral (transfection) or a non-viral (transduction) vector, and by either an in vivo or ex vivogene-transfer strategy. With the in vivo method, which is technically relatively easier, the genetic material is transferred directly into the host; however, there are safety concerns with this approach. The indirect ex vivotechnique requires the collection of cells by tissue harvest, and their genetic modification in vitro before transfer back into the host. Although technically more demanding, it is a safer method, allowing testing of the cells for any abnormal behaviour before reimplantation, and selection of those with the highest gene expression .
Besides the issues of cost, efficacy and biological safety that need to be answered before this strategy of genetic manipulation is applied in humans, delivery of growth factors, particularly BMPs, using gene therapy for bone regeneration has already produced promising results in animal studies [70,71].
In addition to the intrinsic potential of bone to regenerate and to the aforementioned methods used to enhance bone regeneration, adequate mechanical stability by various means of stabilisation and use of fixation devices is also an important element for optimal bone repair, especially in challenging cases involving large bone defects or impaired bone healing. The mechanical environment constitutes the fourth factor of the ‘diamond concept’ of fracture healing, along with osteoconductive scaffolds, growth factors and osteogenic cells, interacting during the repair process .
During bone regeneration, intermediate tissues, such as fibrous connective tissue, cartilage and woven bone, precede final bone formation, providing initial mechanical stability and a scaffold for tissue differentiation. The mechanical loading affects the regeneration process, with different stress distribution favouring or inhibiting differentiation of particular tissue phenotypes . High shear strain and fluid flows are thought to stimulate formation of fibrous connective tissue, whereas lower levels stimulate formation of cartilage, and even lower levels favour ossification .
The interfragmentary strain concept of Perren has been used to describe the different patterns of bone repair (primary or secondary fracture healing), suggesting that the strain that causes healthy bone to fail is the upper limit that can be tolerated for the regenerating tissue . Since then, extensive research on this field has further refined the effects of mechanical stability and mechanical stimulation on bone regeneration and fracture healing . Numerous in vivo studies have shown contradictory results regarding the contribution of strain and mechanical stimulation, in terms of compression or distraction, in bone formation during fracture healing. In early fracture healing, mechanical stimulation seems to enhance callus formation, but the amount of callus formation does not correspond to stiffness . During the initial stages of bone healing, a less rigid mechanical environment resulted in a prolonged chondral bone regeneration phase, whereas the process of intramembranous ossification appeared to be independent of mechanical stability . By contrast, a more rigid mechanical environment resulted in a smaller callus and a reduced fibrous-tissue component . For later stages of bone regeneration, lower mechanical stability was found to inhibit callus bridging and stiffness . Finally, in vitro studies have also shown the role of the mechanical environment on different cell types involved in bone regeneration. It has been demonstrated using cell-culture systems that the different cellular responses in terms of proliferation and differentiation after mechanical stimulation depend on the strain magnitude and the cell phenotype .
Mechanical stability is also important for local vascularisation and angiogenesis during bone regeneration. In an in vivo study, it was shown that smaller interfragmentary movements led to the formation of a greater number of vessels within the callus, particularly in areas close to the periosteum, compared with larger movements , whereas increased interfragmentary shear was associated with reduced vascularisation with a higher amount of fibrous-tissue formation and a lower percentage of mineralised bone during early bone healing .
Finally, the presence of a mechanically stable environment throughout the bone-regeneration process is also essential when additional methods are being used to enhance bone repair [28,79]. Optimal instrumentation with minimal disruption of the local blood supply is required to supplement and protect the mechanical properties of the implanted grafts or scaffolds to allow incorporation, vascularisation and subsequent remodelling .
As an alternative to local augmentation of the bone-regeneration process, the use of systemic agents, including growth hormone (GH)  and parathyroid hormone (PTH)  is also under extensive research. Current evidence suggests a positive role for GH in fracture healing, but there are issues about its safety profile and optimal dose, when systemically administered to enhance bone repair . There are also numerous animal studies and clinical trials showing that intermittent PTH administration induces both cancellous and cortical bone regeneration, enhances bone mass, and increases mechanical bone strength and bone-mineral density, with a relatively satisfactory safety profile [81,82]. Currently, two PTH analogues, PTH 1-34 (or teriparitide) and PTH 1-84, are already used in clinical practice as anabolic agents for the treatment of osteoporosis [81,83], and research is being carried out into their off-label use as bone-forming agents in complex conditions requiring enhancement of bone repair, such as complicated fractures and non-unions.
In addition to the anabolic agents for bone regeneration, current antiresorptive therapies that are already in clinical use for the management of osteoporosis could be used to increase bone-mineral density during bone regeneration and remodelling by reducing bone resorption. Biphosphonates, known to reduce the recruitment and activity of osteoclasts and increase their apoptosis, and strontium ranelate, known to inhibit bone resorption and stimulate bone formation, could be beneficial adjuncts to bone repair by altering bone turnover . In addition, a new pharmaceutical agent called denosumab, which is a fully human monoclonal antibody designed to target receptor activator of nuclear factor-κB ligand (RANKL), a protein that selectively inhibits osteoclastogenesis, might not only decrease bone turnover and increase bone-mineral density in osteoporosis, but also indirectly improve bone regeneration in other conditions requiring enhancement .
Recently, another signalling pathway, the Wnt pathway, was found to play a role in bone regeneration . Impaired Wnt signalling is associated with osteogenic pathologies, such as osteoporosis and osteopenia. Thus, novel strategies that systemically induce the Wnt signalling pathway or inhibit its antagonists, such as sclerostin, can improve bone regeneration. However, there are concerns about carcinogenesis .
Another approach for systemic enhancement of bone regeneration is the use of agonists of the prostaglandin receptors EP2 and EP4, which were found to be skeletally anabolic at cortical and cancellous sites. Promising results have been seen in animal models, without adverse effects, and therefore these receptors may represent novel anabolic agents for the treatment of osteoporosis and for augmentation of bone healing .
Finally, new treatments for systemic augmentation of bone regeneration may come to light while researchers are trying to elucidate the alterations seen at the cellular and molecular level in conditions with increased bone formation capacity. Fibrodysplasia ossificans progressiva, a rare genetic disorder, is an example of how an abnormal metabolic condition can be viewed as evidence for systemic regeneration of large amounts of bone secondary to alterations within the BMP signalling pathway , and may indicate unique treatment potentials.
There are several clinical conditions that require enhancement of bone regeneration either locally or systemically, and various methods are currently used to augment or accelerate bone repair, depending on the healing potential and the specific requirements of each case. Knowledge of bone biology has vastly expanded with the increased understanding at the molecular level, resulting in development of many new treatment methods, with many others (or improvements to current ones) anticipated in the years to come. However, there are still gaps; in particular, there is still surprisingly little information available about the cellular basis for MSC-mediated fracture repair and bone regeneration in vivo in humans. Further understanding in this area could be the key to an improved and integrated strategy for skeletal repair.
In the future, control of bone regeneration with strategies that mimic the normal cascade of bone formation will offer successful management of conditions requiring enhancement of bone regeneration, and reduce their morbidity and cost in the long term. Research is ongoing within all relevant fields, and it is hoped that many bone-disease processes secondary to trauma, bone resection due to ablative surgery, ageing, and metabolic or genetic skeletal disorders will be successfully treated with novel bone-regeneration protocols that may address both local and systemic enhancement to optimise outcome.
The authors declare that they have no competing interests.
RD contributed to the literature review and writing. EJ, DMcG and PVG contributed to the writing of specific sections of the manuscript within their main scientific interest, and critically revised the manuscript for important intellectual content. All authors read and have given final approval of the final manuscript.
The pre-publication history for this paper can be accessed here: